Due to the permanent technical development in tissue through the last years it has to become more and more necessary to obtain creping blades with a longer life-time and special applications. Get in touch and try the improved creping blades with a ceramic or tungsten carbid coating on the top.
Please take further technical facts from our datasheet at the end of the page.
Alloy No.:
1.0605 (AISI 1075)
Description:
C 75 S
Hardness:
HRC: 48 – 52
HV: 490 – 550
Tensile strength:
1600 – 1800 N/mm²
Length:
after your specification
Standard width in mm:
100 / 110 / 114 / 120 / 125
Standard thickness in mm:
0.9 / 1.0 / 1.25 / 1.5
Surface:
blue polished
Design:
with cut edges, straightened
straightened, grinded 90° on both sides
with one or both sides bevelled from 50° – 85°
Substrate:
Carbon steel
Lay:
Ceramic
Hardness Ceramic:
approx. 1000 HV
Colour Ceramic:
grey
Alloy No.:
1.0605 (AISI 1075)
Description:
C 75 S
Hardness:
HRC: 48 – 52
HV: 490 – 550
Tensile strength:
1600 – 1800 N/mm²
Length:
after your specification
Standard width in mm:
100 / 110 / 114 / 120 / 125
Standard thickness in mm:
0.9 / 1.0 / 1.25 / 1.5
Surface:
greyish blue
Design:
with cut edges, straightened
straightened, grinded 90° on both sides
with one or both sides bevelled from 50° – 85°
Substrate:
Carbon steel
Lay:
Ceramic
Hardness Ceramic:
approx. 1000 HV
Colour Ceramic:
grey
Alloy No.:
1.0605 (AISI 1075)
Description:
C 75 S
Hardness:
HRC: 48 – 52
HV: 490 – 550
Tensile strength:
1600 – 1800 N/mm²
Length:
after your specification
Standard width in mm:
100 / 110 / 114 / 120 / 125
Standard thickness in mm:
0.9 / 1.0 / 1.25 / 1.5
Surface:
bright polished
Design:
with cut edges, straightened
straightened, grinded 90° on both sides
with one or both sides bevelled from 50° – 85°
Substrate:
Carbon steel
Lay:
Ceramic
Hardness Ceramic:
approx. 1000 HV
Colour Ceramic:
grey
Alloy No.:
1.1274 (AISI 1095)
Description:
C 100 S
Hardness:
HRC: 52 – 55
HV: 550 – 600
Tensile strength:
1800 – 2000 N/mm²
Length:
after your specification
Standard width in mm:
100 / 110 / 114 / 120 / 125
Standard thickness in mm:
0.9 / 1.0 / 1.25 / 1.5
Surface:
blue polished
Design:
with cut edges, straightened
straightened, grinded 90° on both sides
with one or both sides bevelled from 50° – 85°
Substrate:
Carbon steel
Lay:
Ceramic
Hardness Ceramic:
approx. 1000 HV
Colour Ceramic:
grey
Alloy No.:
1.1274 (AISI 1095)
Description:
C 100 S
Hardness:
HRC: 52 – 55
HV: 550 – 600
Tensile strength:
1800 – 2000 N/mm²
Length:
after your specification
Standard width in mm:
100 / 110 / 114 / 120 / 125
Standard thickness in mm:
1.0 / 1.25 / 1.5
Surface:
greyish blue
Design:
with cut edges, straightened
straightened, grinded 90° on both sides
with one or both sides bevelled from 50° – 85°
Substrate:
Carbon steel
Lay:
Ceramic
Hardness Ceramic:
approx. 1000 HV
Colour Ceramic:
grey
Alloy No.:
1.1274 (AISI 1095)
Descripstion:
C 100 S
Hardness:
HRC: 52 – 55
HV: 550 – 600
Tensile strength:
1800 – 2000 N/mm²
Length:
after your specification
Standard width in mm:
100 / 110 / 114 / 120 / 125
Standard thickness in mm:
0.9 / 1.0 / 1.25 / 1.5
Surface:
bright polished
Design:
with cut edges, straightened
straightened, grinded 90° on both sides
with one or both sides bevelled from 50° – 85°
Substrate:
Carbon steel
Lay:
Ceramic
Hardness Ceramic:
approx. 1000 HV
Colour Ceramic:
grey
Alloy No.:
1.4021 (AISI 420)
Description:
X20Cr13
Hardness:
HRC: 47 – 50
HV: 470 – 520
Tensile strength:
1600 – 1800 N/mm²
Length:
after your specification
Standard width in mm:
100 / 114 / 120 / 125
Standard thickness in mm:
1.25
Surface:
bright polished
Design:
with cut edges, straightened
straightened, grinded 90° on both sides
with one or both sides bevelled from 50° – 85°
Substrate:
Stainless steel
Lay:
Ceramic
Hardness Ceramic:
approx. 1000 HV
Colour Ceramic:
grey
Alloy No.:
2.1020 (bronze)
Description:
Cu Sn 6
Hardness:
HB: 200 – 230
Tensile strength:
650 – 740 N/mm²
Length:
after your specification
Standard width in mm:
100 / 114 / 120 / 125
Standard thickness in mm:
1.0 / 1.2 / 1.5
Surface:
bronze
Design:
with cut edges, straightened
straightened, grinded 90° on both sides
with one or both sides bevelled from 50° – 85°
Substrate:
bronze
Lay:
Ceramic
Hardness Ceramic:
approx. 1000 HV
Colour Ceramic:
grey
Advantages of Creping Blades with Ceramic or Tungsten Carbid:
- high wear resistance
Please note the following packaging references.
Our datasheet: Creping Blades with Ceramic
(09/2015)